| Product Shopping Guide |
 |
 Cold-Work Die Steel Hot-Work Die Steel
Die Steel for Plastic Industry High Speed Tool Steel |
|
| The similar grades of foreign countries |
China
4Cr5MoSiV1 |
America
H13 |
Japan
SKD61 |
German
X40CrMoV51
(1.2344) |
Bohler
W302 |
|
Chemical component (%) |
|
Standard |
C |
Mn |
Si |
Cr |
P |
S |
Mo |
V |
|
GB/T1299-2000 |
0.32-0.45 |
0.20
/0.50 |
0.80
/1.20 |
4.75
/5.50 |
<=0.030 |
<=0.030 |
1.10
/1.75 |
0.80
/1.20 | |
|
Specialty |
Harden and air cooling steel, 600`C work, high rigidity, high endurance, anti-heating, anti-cracking, electric sediment and middle-melting steel, compact structure, refined in electric cooker, quality of steel is pure, owned good character of equal direction |
|
Use |
Extrusion mold of aluminum and magnesium, die-casting mold, especially adapt to the mold in large and complicated form. |
|
Extrusion mold of copper alloy, die-casting mold |
|
Hot pressing machine mold |
|
Heat treatment |
Quench:1000-1040`C via 600`C and 850`C, preheating oil or wind cooling |
|
Temper temperature and rigidity HBC(reference) |
|
quench hardening |
108-300`C |
450-500`C |
550-5700`C |
|
53-55 |
51-52 |
53-54 |
50-52 | |
|
Temper temperature should be higher than working temperature in order to stabilize the working size of mold |
|
Heat up to 650`C of average temperature in order to eliminate the machined stress, 500`C air cooling after electric cooker cooling |
|
Tempering, 800-850`C,slow cooling after diathermia |
|
Dimension(mm) |
Round: ¦Õ60-¦Õ400 Flat :20-80*40-800 80-300*500-800 |
|
The state of leaving factory |
HBS<=235 |
| The similar grades of foreign countries |
China
3Cr2W8V |
America
H21 |
Japan
SKD5 |
German |
Bohler |
|
Chemical component (%) |
|
Standard |
C |
Mn |
Si |
Cr |
P |
S |
W |
V |
|
GB/T1299-2000 |
0.30
/0.40 |
<=0.40 |
<=0.40 |
2.20
/2.70 |
<=0.030 |
<=0.030 |
7.50
/9.00 |
0.20
/0.50 | |
|
Specialty |
Better performance of high temperature and mechanics, better permanence |
|
Use |
Pressing machine die-casting mold, hot extruding dies, heading die, cutting die, die-casting mold |
|
Heat treatment |
Quench:1050-1150`C,oil cooling, rigidity is 40-50HRC |
|
Temper temperature:550-650`C, temper two times, every time two hours, temper rigidity 40-50HRC |
|
Annealing: anneal in isothermal temperature and heating temperature 840-880`C, isothermal temperature720-740`C,anneal rigidity<=241HB |
|
Dimension(mm) |
Round:¦Õ50-¦Õ280 Flat:20-300*40-610 |
|
The state of leaving factory |
HBS255-207 |
| The similar grades of foreign countries |
China
5CrNiMo |
America
L6 |
Japan
SKT4 |
German
1.2713 |
Bohler |
|
Chemical component (%) |
|
Standard |
C |
Mn |
Si |
Cr |
P |
S |
Ni |
Mo |
|
GB/T1299-2000 |
0.50
/0.60 |
0.50
/0.80 |
<=0.40 |
0.50
/0.80 |
<=0.030 |
<=0.030 |
1.40
/1.80 |
0.15
/0.30 | |
|
Specialty |
high rigidity, high endurance, a certain endurance, good penetration |
|
Use |
Swage in small and middle size, length of side<=300mm,working temperature<500`C |
|
Heat treatment |
Quench:820-860`C,HRC38-42 |
|
Temper:520-540`C,HRC38-42 |
|
Dimension(mm) |
Round:¦Õ100-¦Õ400 Flat:20-300*40-800 |
|
The state of leaving factory |
HBS241-197 |
| The similar grades of foreign countries |
China
5CrMnMo |
America
6G |
Japan
SKT5 |
German |
Bohler |
|
Chemical component (%) |
|
Standard |
C |
Mn |
Si |
Cr |
P |
S |
Mo |
|
GB/T1299-2000 |
0.50
/0.60 |
1.20
/1.60 |
0.25
/0.60 |
0.60
/0.90 |
<=0.030 |
<=0.030 |
0.15
/0.30 | |
|
Specialty |
high rigidity, high endurance, a certain endurance, good penetration |
|
Use |
Swage in small and middle size, hot extruding dies |
|
Heat treatment |
Quench:820-860`C,oil cooling |
|
Temper: HRC62 |
|
Dimension(mm) |
Round:¦Õ100-¦Õ400 Flat:20-300*40-800 |
|
The state of leaving factory |
Spheroidal anneal HBS210 | | |
|
|
|